PA6T/6I copolymer series
+
  • PA6T/6I copolymer series

PA6T/6I copolymer series

SL HTPA is an industrial high-temperature nylon chip made from hexamethylenediamine, terephthalic acid, isophthalic acid, adipic acid, caprolactam, and decamethylenediamine through salification, polymerization, drying, and granulation. It has advantages such as high temperature resistance, corrosion resistance, and low water absorption, and can meet the production requirements of extrusion, injection molding, and molding. It is widely used in precision molding injection parts in the fields of electronic connectors, LEDs, and low-voltage electrical appliances, as well as high-temperature resistant parts around automobile engines, and fuel tanks and pipelines resistant to fuel and solvents. This series has the highest high-temperature rigidity and the lowest water absorption rate among the existing grades of Sanli New Materials. It has stable mechanical properties and excellent chemical resistance in both dry and humid environments.
Inquiry
Contact Us
  • Product Description
    • Commodity name: PA6T/6I copolymer series

    SL HTPA is an industrial high-temperature nylon chip made from hexamethylenediamine, terephthalic acid, isophthalic acid, adipic acid, caprolactam, and decamethylenediamine through salification, polymerization, drying, and granulation. It has advantages such as high temperature resistance, corrosion resistance, and low water absorption, and can meet the production requirements of extrusion, injection molding, and molding. It is widely used in precision molding injection parts in the fields of electronic connectors, LEDs, and low-voltage electrical appliances, as well as high-temperature resistant parts around automobile engines, and fuel tanks and pipelines resistant to fuel and solvents. This series has the highest high-temperature rigidity and the lowest water absorption rate among the existing grades of Sanli New Materials. It has stable mechanical properties and excellent chemical resistance in both dry and humid environments.

    High-temperature resistant nylon resin
      PA6T/6I/66 Copolymer SeriesPA6T/6I Copolymer Series
    Test ItemTest Standard13451357
    Melting Point/℃GB/T 19466.3-2004312325
    Glass Transition Temperature (Midpoint)/℃GB/T 19466.3-2004125135
    Density/g▪cm -3GB/T 1033.1-20081.151.15
    Ash Content/%GB/T 9345.1-20080.150.15
    Water Absorption at 23℃, 24h/%GB/T 1034-20080.300.20
    Moisture Content/%Sanli Enterprise Standard0.300.30
    Remarksa. Residue after calcination at 800℃ for 4h
    b. Water absorption data are typical values after heat treatment
    c. Weight loss after drying at 150℃ for 2h