- Product Description
-
- Commodity name: PA1055
SL HTPA is an industrial high-temperature nylon chip made from ethylenediamine, terephthalic acid, isophthalic acid, adipic acid, caprolactam, and decamethylenediamine through salification, polymerization, drying, and granulation. It has advantages such as high temperature resistance, corrosion resistance, and low water absorption, and can meet the production requirements of extrusion, injection molding, and molding. It is widely used in precision molding injection parts in the fields of electronic connectors, LEDs, and low-voltage electrical appliances, as well as high-temperature resistant parts around automobile engines, and fuel tanks and pipelines resistant to fuel and solvents.
High-Temperature Resistant Nylon Resin PA1055 Test Item Test Standard 1055 Melting Point/℃ GB/T 19466.3-2004 311 Glass Transition Temperature (Midpoint)/℃ GB/T 19466.3-2004 110 Density/g▪cm -3 GB/T 1033.1-2008 1.15 Ash Content/% GB/T 9345.1-2008 0.15 Water Absorption at 23℃, 24h/% GB/T 1034-2008 0.10 Moisture Content/% Sanli Enterprise Standard 0.3 Remarks a. Residue after calcination at 800℃ for 4h b. Water absorption data are typical values after heat treatment c. Weight loss after drying at 150℃ for 2h
Inquiry
CONTACT US